Typical Properties
Density
1.19 g/cm³
Density - Specific Gravity
1.19 g/cm³
Change in Volume (in Reference Fuel B, 27 °C, 168 hr)
30 %
Change in Volume (in Reference Fuel B, 27 °C, 168 hr)
30 %
Change in Volume (in ASTM #1 Oil, 100 °C, 168 hr)
-10 %
Change in Volume (in ASTM #1 Oil, 100 °C, 168 hr)
-10 %
Change in Volume (in IRM 903 Oil, 100 °C, 168 hr)
27 %
Change in Volume (in IRM 903 Oil, 100 °C, 168 hr)
27 %
Change in Volume (in Water, 100 °C, 168 hr)
12 %
Change in Volume (in Water, 100 °C, 168 hr)
12 %
Melt Viscosity (190 °C, 300 sec^-1)
545 Pa·s
Tensile Stress at 100% (1.90 mm)
3.90 MPa
Tensile Stress at 100% (1.90 mm)
3.90 MPa
Tensile Stress at 100% (125 °C, 1.90 mm)
3.90 MPa
Tensile Stress at 100% (125 °C, 1.90 mm)
3.90 MPa
Tensile Stress at Yield (1.90 mm)
9.60 MPa
Tensile Stress at Yield (125 °C, 1.90 mm)
10.6 MPa
Tensile Strength at Yield (1.90 mm)
9.60 MPa
Tensile Strength at Yield (125 °C, 1.90 mm)
10.6 MPa
Tensile Strain at Break (1.90 mm)
300 %
Tensile Strain at Break (125 °C, 1.90 mm)
330 %
Torsion Modulus (24 °C, 1.9 mm)
1.9 MPa
Torsion Modulus (-20 °C, 1.9 mm)
7.5 MPa
Tensile Set
8 %
Clash-Berg Modulus (-38 °C)
68.9 MPa
Tensile Elongation at Break (125 °C, 1.90 mm)
330 %
Tensile Elongation at Break (1.90 mm)
300 %
Tear Strength (Die C, 1.90 mm)
26.3 kN/m
Ductile/Brittle Transition Temperature
-51 °C
Ductile/Brittle Transition Temperature
-51 °C
Change in Shore Hardness in Air (Shore A, 125 °C, 168 hr)
5.0
Shore Hardness (Shore A, 1.90 mm, Compression Molded)
62
Change in Durometer Hardness in Air (Shore A, 125 °C, 168 hr)
5.0
Durometer Hardness (Shore A, 1.90 mm, Compression Molded)
62
Compression Set (24 °C, 22 hr, Method B)
15 %
Compression Set (100 °C, 22 hr, Method B)
55 %
Compression Set (24 °C, 22 hr)
15 %
Compression Set (100 °C, 22 hr)
55 %
Taber Abrasion Resistance (CS-17 Wheel, 1000 g, 1000 Cycles)
7.00 mg
Melt Temperature
177 °C